Ceramic is increasingly used for balls on account of its exceptional powers of resistance thus satisfying many requirements. Resistant, generating low friction, light and enabling high precision uses, these balls are used in watch making, the medical and automotive sectors, high pressure pumps, high precision bearings etc.
| Propriétés physiques | Saphir | Rubis | Alumine | Nitrure de Silicium HP | Zircone Y-TZP | Carbure de Tungstène * | Acier Inox * | Acier 100Cr6 * |
|---|---|---|---|---|---|---|---|---|
| Structure cristalline | Mono | Poly | Poly | Poly | Poly | Poly | Poly | |
| Formule chimique | Al2O3 | Cr2O3 | Al2O3 | Si3N4 | ZrO2 | Wc (6T10) | ||
| Pureté % | 99,99 % | 99 % | 1,00 | 90 | 90 à 95 | Wc94+C06 | ||
| Masse volumique (Kg/dm3) | 3,99 | 3,90 | 3,10 à 3,20 | 6 | 15 | 8 | 7,85 | |
| Dureté (HV) | 2 300 | 1650,00 | 1 600 | 1 100 à 1 500 | 1 550 | 500 à 800 | 762 à 865 | |
| Résistance à la compression (MPa) | 2 100 | 2400,00 | 3 000 | ≈ 4 000 | 5 300 | - | 2 240 | |
| Résistance élastique (MPa) | - | 280,00 | 400 | - | - | 500 à 1 500 | ||
| Résistance à la flexion (MPa) | 390 | 470,00 | 1 000 | 700 à 1 100 | 1 900 | - | ||
| Résilience KIC (MPa.m1/2) | 1 | 4,00 | 6 | 10 | - | 30-80 | ||
| Module de young (module d'élasticité) (GPa) | 430 | 380,00 | 320 | 200 | 610 | 200 | 205 | |
| Coef. d'expansion thermique (10-6 .°K-1) | 5,3 | 5,50 | 3,2 | 10 | 5,5 | 10 à 12 | ||
| Conductivité thermique (W/m°K) | 36 | 29,00 | 40 | 2 | 80 | - | ||
| Capacité thermique (J/Kg°K) | 755 | 900,00 | 750 | 500 | 201 | - | ||
| Température max. d'utilisation (°C) | 1 800 à 2 000 | 1 500 à 1 800 | 1 200 à 1500 | 1 000 | - | 300 à 600 | 450 | |
| Résistance aux acides | Très bonne | Très bonne | Très bonne | Bonne | Limitée | Limitée | Non résistant | |
Download the technical data sheet :